Sign In | Join Free | My carsrow.com |
|
Brand Name : TANKII
Model Number : CuMn12Ni
Certification : ISO
Place of Origin : China
MOQ : 20kg
Payment Terms : T/T,L/C,Western Union
Supply Ability : 60,000kg/Month
Packaging Details : Wire diameter 0.02mm-1.0mm packing in spool, big than 1.0mm packing in coil
Price : 5-7USD/KG
Delivery Time : 10-15Days
Advantage : Good Price
Type : Nickel Pipe/ Tube
Manufacturer : Tankii Alloy
Product Name : Low Resisitance Nickel Copper Alloy Wire (CuNi15) with Factory price
Main Market : Globle
Resistivity : 231.5 to 23.6 Ohm. Mm2/ft
Alloy Grades : CuNi1, CuNi2, CuNi6, CuNi8, CuNi14, CuNi19, CuNi23, CuNi30, CuNi34, CuNi44
Manufacturer Location : China
Ni-Cr: Cr20Ni80,Cr15Ni60, Cr20Ni35, Cr25Ni20 etc.
Nichrome,a non-magnetic alloy of nickel and chromium, is commonly used to make resistance wire because it has a high resistivity and resistance to oxidation at high temperatures.
FeCrAl: 1Cr13AI4, 0Cr19AI2, 0Cr15AI5, 0Cr20AI5, 0Cr25AI5, 0Cr21AI6 Nb,OCr27Al7Mo2
FeCrAl, a family of iron-chromium-aluminum alloys used in a wide range of resistance and high-temperature applications is also used in the form of resistance wires.
Size
Wire: 0.018mm-10mm
Ribbon: 0.05*0.2mm-2.0*6.0mm
Strip: 0.5*5.0mm-5.0*250mm
Bar: 10-100mm
Product Parameters
1 Excellent resistance to oxidation under heating condition;
2 High resistance and long lifetime;
3 Low temperature coefficient;
4 Good performance of anti-carburizing, the atmosphere and surface of sulfur pollution.
Main characteristic of FeCrAl electric heating alloy wire | ||||||||
Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
Nb0.5 | Mo1.8-2.2 | |||||||
Max. continuous service temp. (° C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resistivity at 20º C(μ Ω @ m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
Thermal conductivity(KJ/m@ h@ º C) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
Coefficient of lines expansion(α × 10-6/º C) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
Melting point approx. ( º C) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Elongation at rupture(%) | > 16 | > 12 | > 12 | > 12 | > 12 | > 12 | > 10 | |
Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Repeat Bending frequency(F/R) | > 5 | > 5 | > 5 | > 5 | > 5 | > 5 | > 5 | |
Hardness(H. B. ) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
continuous servicetime(Hours/ º C) | -- | ≥ 80/1300 | ≥ 80/1300 | ≥ 80/1300 | ≥ 80/1250 | ≥ 50/1350 | ≥ 50/1350 | |
Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
![]() |